高温蒸汽腐蚀,high temperature steam corrosion
1)high temperature steam corrosion高温蒸汽腐蚀
1.In order to analyze the reason of the boiler\"s water wall tube bursting,macrostructure,chemical composition check,metallographic check,tensile testing at ambient temperature and other tests are made,and the results are indicated that thehigh temperature steam corrosion and hydrogen damage of the rough tube wall which was caused by overheating welding is the main cause of the tube bursting.采用宏观检查、化学成分分析、机械性能测试、金相分析等方法对锅炉水冷壁爆管原因进行分析,各项检验结果表明,在焊接过热形成的粗糙内壁处发生高温蒸汽腐蚀及氢损伤是导致该水冷壁管爆管的主要原因。
2)high-pressure steam etching高压蒸汽腐蚀
3)hot steam corrosion热蒸汽腐蚀
4)high-temperature corrosion高温腐蚀
1.Investigations on outer thermal spraying and inner shot blasting on boiler tube to promotehigh-temperature corrosion resistance;采用外壁喷涂与内壁喷丸方法提高锅炉高温受热面管抗高温腐蚀性能的试验
2.The large amount of vanadium in Orimulsion may cause unexpected problems in the prevention ofhigh-temperature corrosion of furnace.奥里油中含钒量较多,是锅炉预防高温腐蚀设计中的大难题。
3.The mechanism ofhigh-temperature corrosion on water-wall of coal-fired boilers in thermal power plants has been briefly presented, and preventive countermeasures being put forward directing against different causes ofhigh-temperature corrosion, the prevention technology of spraying corrosion-resistant metallic coatings onto surface of the water-wall being emphatically narrated.简要介绍了火电厂燃煤锅炉水冷壁高温腐蚀机理,并针对不同的高温腐蚀原因提出了防护对策。
英文短句/例句
1.The Study on Cure of High-temperature Corrosion in 50MW Generating Unit Boiler;50MW机组锅炉高温腐蚀研究与治理
2.High Temperature Corrosion Research of Sichuan-Chongqing Region 670t/h Boiler Made in China川渝地区国产670t/h锅炉高温腐蚀研究
3.High temperature corrosion resistance of pack aluminized SUS316ss steelSUS316ss钢包埋粉末渗铝的高温腐蚀研究
4.Study on The High Temperature Corrosion Resistance Performance of Two Hot Spray Coatings两种热喷涂层的耐高温腐蚀性能研究
5.Experimental Study on Prevention and Cure of the High Temperature Corrosion and Gas Temperature Deviation;防治高温腐蚀及炉膛出口烟温偏差试验研究
6.Process of High-Hardness and High-Temperature Erosion Resistance Enamel on Steel;高硬度耐高温腐蚀搪瓷层制备工艺研究
7.The Analysis and Countermeasure for the Crude Oil with High TAN in CDU加工高酸原油常减压装置高温腐蚀分析及对策
8.A High Degree of Corrosion Resistance,Temperature Resistance,Wear Resistance,High Toughness Heavy Duty Coatings:ChemLINE 784高度耐腐蚀、耐温、耐磨、高韧性重防腐蚀涂料ChemLINE 784
parison of high temperature and high pressure corrosion behavior of 16Mn steel in different corrosive environment不同腐蚀介质中16Mn钢高温高压腐蚀行为的比较
10.THE STUDY ON THE SPRAY CORED WIRES FOR HIGH TEMPERATURE EROSION-CORROSION RESISTANCE;耐高温冲蚀—热腐蚀热喷涂粉芯线材的研究
11.The product is manufactured with imported raw material and features high pressure and corrosion resistance.该产品是选用进口材料,耐高温、腐蚀。
12.HIGH TEMPERATURE OXIDATION AND CHLORINATION OF METALLIC MATERIALS;几种金属材料的高温氧化、氯化腐蚀
13.Study on the Corrosion of Carbon Steel in Simulated Boiler Water;关于高温模拟炉水中碳钢的腐蚀研究
14.Hot Corrosion of Superalloy Sprung Parts in a Kiln Crown铠装窑高温合金挂件热腐蚀失效分析
15.Study on performance of corrosion protection of silicone heat resistant coating有机硅耐高温涂料的防腐蚀性能研究
16.Experiment on the Anti-corrosion Property of Chrome Molybdenum Steel Tube in Naphthenic Acid Environment铬钼钢管耐高温环烷酸腐蚀性能试验
17.New Type of High Temperature and Corrosion Resistance Coating Material--Ceramic Plastic新型耐高温耐腐蚀涂层材料——陶瓷塑料
18.Selection of Materials of Cast Iron Crucible for High-Temperature Aluminum Melting with Respect to Corrosion Resistance从耐腐蚀性能看高温熔铝坩埚的选材
相关短句/例句
high-pressure steam etching高压蒸汽腐蚀
3)hot steam corrosion热蒸汽腐蚀
4)high-temperature corrosion高温腐蚀
1.Investigations on outer thermal spraying and inner shot blasting on boiler tube to promotehigh-temperature corrosion resistance;采用外壁喷涂与内壁喷丸方法提高锅炉高温受热面管抗高温腐蚀性能的试验
2.The large amount of vanadium in Orimulsion may cause unexpected problems in the prevention ofhigh-temperature corrosion of furnace.奥里油中含钒量较多,是锅炉预防高温腐蚀设计中的大难题。
3.The mechanism ofhigh-temperature corrosion on water-wall of coal-fired boilers in thermal power plants has been briefly presented, and preventive countermeasures being put forward directing against different causes ofhigh-temperature corrosion, the prevention technology of spraying corrosion-resistant metallic coatings onto surface of the water-wall being emphatically narrated.简要介绍了火电厂燃煤锅炉水冷壁高温腐蚀机理,并针对不同的高温腐蚀原因提出了防护对策。
5)high temperature corrosion高温腐蚀
1.Study onhigh temperature corrosion resistance of FeCrAl and NiCr alloy coating;FeCrAl和高镍铬合金涂层的抗高温腐蚀性能研究
2.High Temperature Corrosion of Superheater Tube Materials in Pulverized Coal-Fired Environment;粉煤燃烧环境中过热器管材的高温腐蚀
3.Cause analysis ofhigh temperature corrosion and precautionary measures for a 300MW boiler furnace;燃煤锅炉炉膛高温腐蚀原因及对策
6)corrosion at high temperature高温腐蚀
1.This paper represents the mechanism of the water wall tubecorrosion at high temperature and the principle of spraying Ni-Cr alloy anticorrosion coat , and introduces the characteristics of the high speed arc spraying and construction technology , at the same time also introduces the method of coat quality inspection.初步阐述了水冷壁管高温腐蚀的机理及喷涂Ni-Cr合金防腐涂层的原理,介绍了高速电弧喷涂技术的特点、施工工艺,同时也介绍了涂层质量的检测方法。